You will be pleased to note that our LOW SHRINK GRAY, FIRM and FLEX grades all demonstrate controlled shrink. You will never encounter variations in hardness or shrink with Akron Jewelry Rubber™.
Pre-heat your vulcanizer to 310° F (154° C). Periodic checks of temperature calibration are recommended. Temperature and time may be varied to suit your needs and experience, however, it is recommended that you not exceed 325° F (163°C) with any natural mold rubber.
Akron Jewelry Rubber™ should be vulcanized at 310° F (154°C) for 7½ minutes per layer of rubber.
Remove plastic covers from both sides of rubber. A good practice is to use stainless steel or aluminum mold plates which are available inexpensively from any dealer. If you write on the rubber, slip a small piece of aluminum foil or parchment paper between the rubber and the mold plate to prevent ink transfer. Pack mold frames fully, taking care to fill undercuts with small pieces of rubber.
It is not necessary in all cases to pack an extra layer of rubber (7 pieces in a ¾ frame). If you use frames with small vent holes, it is a good practice to do so. In any case, you should make certain that the rubber in your packed frame extends above the surface of the frame.
Be sure that your vulcanize is up to temperature before inserting packed mold frame.
Tighten vulcanize by hand and check periodically during the first 5 minutes to ensure that it remains snug. Do not use excessive pressure as you can damage the model and the vulcanizer.
At the end of an appropriate vulcanization time, remove your mold from the frame and allow cooling at room temperature until it can be handled comfortably. A ¾ (19mm) mold will take about 20 minutes to cool sufficiently. You may also use cold water to cool the mold.
Akron Jewelry Rubber™ provides a somewhat easier release than other products, however you may find that using our slick™ silicone mold release is helpful if used sparingly. As with any mold release spray, allow the spray to dry before injecting wax. Used sparingly, drying is rapid. The wetness you see is the solvent that carries the silicone. The silicone remains in the mold after the solvents dry. Injecting a mold that is still quite wet can produce less than desired results.
Finished molds should be stored away from sunlight and heat to preserve their flexibility for years to come. The uncured shelf life of Akron Jewelry Rubber is 6 years.
Eliminates the major drawback of silicone rubber: TEARING!
Has 4 times the tear resistance of other silicone mold rubber products.
Raises Productivity By 300% Or More!
Works like putty. No cutting or snipping to fit pattern. Just spread quickly with fingers, insert model, spread more rubber on top, and vulcanize.
Produces Smooth As Glass Waxes
The surface of your wax patterns will be extraordinarily smooth, finishing time will be minimal.
No Mold Release Required
Wax will not stick to our 4X Silicones. Double your wax injection through-put, as waxes release so readily.
Perfect For Fine Detail
Ingredient balance is fine-tuned to produce super clean detail with even the most intricate designs.
AVAILABLE IN 2.27 kg. (5 LB.) BOXES
12 boxes in a case or special order 50 lb. Bulk pack
Sheet Dimensions: 3/8" x 8" x 9"